1.5223, DIN 42MnV7
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
1.5223, DIN 42MnV7
Designation by Standards
Brand Name | LH No. | Mat. No. | DIN | EN | AISI |
VMV175 | 708 | 1.5223 | 42MnV7 | - | - |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
0.41 | 0.25 | 1.75 | - | - | - | 0.10 | - | - |
Description
VMV175 is a heat treatable, low steel/" target="_blank" class="keylink">alloy steel containing manganese and vanadium.
Applications
Low and moderately stressed components for vehicles, machines and engines.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Soft Annealing
Heat to 640-780oC, cool slowly. This will produce a maximum Brinell hardness of 217.
Normalizing
Temperature: 860-890oC.
Hardening
Harden from a temperature of 850-880, 840-870oC followed by oil or water quenching.
Tempering
Tempering temperature: 480-650oC.
Forging
Hot forming temperature: 1100-850oC.
Machinability
Machining is best done with this alloy in the annealed or normalized and tempered condition. It can be machined by all conventional methods.
Mechanical properties
Heat treatment
Machining
Welding performance