EN9 Carbon Steel
Production specification
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
EN9 Carbon Steel
EN9 is an unalloyed medium carbon steel. It is supplied at the hardness obtained after hot rolling or cold drawing, with a hardness normally within the range of 180 to 230HB. EN9 is available from stock in bar and can be cut to your requirements. We also offer EN9 plate flame cut to your required sizes and normalised. |
TYPICAL ANALYSIS |
|
|
||
C. |
Si. |
Mn. |
S. |
P. |
0.50% |
0.25% |
0.70% |
0.05% |
0.05% |
Forging:
Heat slowly and uniformly to 1100°C. After forging cool slowly.
Annealing:
Heat uniformly to 700°C. Soak well and cool slowly in the furnace.
Hardening:
Heat uniformly to 820/840°C until heated through. Quench in oil, or water.
Tempering:
Heat uniformly and thoroughly at the selected tempering temperature, between 550/660°C and hold at heat for one hour per inch of total thickness.
Hard Chromium Plating:
After hard chromium plating, the steel should be tempered for approximately 4 hours at 180°C, in order to avoid hydrogen embrittlement.
Welding:
Firstly heat to approximately 100-350°C. Use an unalloyed basic electrode, for welding unalloyed structural steels.
Normalising:
Normalise at 840-870°C, and cool in air.
Stress Relieving:
After rough machining tools should be stress relieved. Soaking time 2 hours after the whole piece has attained a temperature of approximately 675°C. Cool in furnace to approximately 500°C, and then freely in air.
Physical Properties:
Density |
Coefficient of Thermal Expansion |
Modulus of Elasticity |
kg/m |
per c from 20 c |
N/mm |
7800 |
11.6x10-6 |
206000 |
Mechanical properties
Heat treatment
Machining
Welding performance